Zinc spray

Name: Zinc spray
Brand: Würth
SKU: 0893113114

Zinc spray
ZNSPR-LIGHT/ALUZINC-400ML

Art.-no. 0893113114

EAN 4061975341396

All versions

Similar products

Prices for customers after login

Zinc spray

Art.-no. 0893113114

Prices for customers after login

Quantity

Exclusively for trade customers

Locate trade store
Login/Register
Call customer service: +371 67788996

Long-term protection and repair of metallic surfaces

Excellent corrosion protection

The metal is actively protected, even with minor damage

Over 100 hours of salt-spray resistance (DIN 50021 SS)

Excellent adhesive properties on bare metal

Excellent spot welding properties

Notice

Not suitable as a primer for PU, MS polymer or hybrid sealing compounds.

Do not paint over with other paints

The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.

Product information

Würth Catalogue

Datasheets(X)

Safety data sheet

Certificates/ Documents

Application area

For visual enhancement, repair and protection against corrosion of metallic surfaces.

Instructions

The optimal application temperature is between 15°C-25°C

Contents	400 ml
Chemical basis	Alkyd resin combination
Colour	Zinc, bright
Min. curing time	10 h
Fully hardening/curing conditions	At recommended dry layer thickness
Max. curing time	12 h
Resistance in salt-spray test	100 h
Max. temperature resistance	240 °C
Dust-drying time	15 min
Dry layer thickness (first back-and-forth motion)	30 µm
Conditions for dust-drying time	at recommended dry layer thickness
Purity rating zinc	99.995 %
Zinc content in the dry film	44.6 %
Coating thickness	70 µm
Recoatable/Can be painted over	Conditional, preliminary testing required
Grip strength conditions	at recommended dry layer thickness
Substrates with good adhesion	PMMA, Polycarbonate, Polystyrene, Zinc plated surfaces
Spot weldable	Yes
AOX-free	Yes
Cross-cut test	MAN 0-1
Min./max. grip strength	15-20 min
Cross-cut test conditions	in accordance with DIN 53151
Conditions for resistance in salt-spray test	in accordance with DIN 50021
Min./max. processing temperature	5 to 35 °C
Shelf life from production	30 Month
Conditions to maintain shelf life from production	at 10°C to 25°C
Min. flashing point	-42 °C

Suitable glove:

Product

Description

Nitrile chemical protective glove With cotton velour finish inside

Description:

Permeation level: 1

Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.

Measured breakthrough time

Permeation level

< 10 min

≥ 10 min

≥ 30 min

≥ 60 min

≥ 120 min

≥ 240 min

≥ 480 min

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.